| Автори: Пашински, Ч. О. Заглавие: Механични свойства на Cr/CrN/CrAlN покритие, нанесено чрез нискотемпературно магнетронно разпрашване върху бързорезна стомана P6M5 Ключови думи: Chromium Aluminium Nitride, Hard Coatings, PVD, CFUBMS Абстракт: Multilayer hard coatings for cutting tools are currently widespread. When they are applied on high-speed and other steels, there is a growing need for the deposition process to occur at lower temperatures to prevent phase transformations in the substrate (and a decrease in its hardness respectively). However, these lower temperatures could often compromise the applied coating, primarily its adhesion. In this study, one Cr/CrN/CrAlN coating deposited by magnetron sputtering on high-speed steel P6M5 at a temperature up to 200 °C is considered. By using an appropriate compositional gradient in its layers, a good adhesion to the substrate is achieved. Библиография Издание
| Autors: Pashinski, C. O. Title: Mechanical properties of Cr/CrN/CrAlN coating on P6M5 high-speed steel deposited by low-temperature magnetron sputtering Keywords: Chromium Aluminium Nitride, Hard Coatings, PVD, CFUBMS Abstract: Multilayer hard coatings for cutting tools are currently widespread. When they are applied on high-speed and other steels, there is a growing need for the deposition process to occur at lower temperatures to prevent phase transformations in the substrate (and a decrease in its hardness respectively). However, these lower temperatures could often compromise the applied coating, primarily its adhesion. In this study, one Cr/CrN/CrAlN coating deposited by magnetron sputtering on high-speed steel P6M5 at a temperature up to 200 °C is considered. By using an appropriate compositional gradient in its layers, a good adhesion to the substrate is achieved. References Issue
|
Вид: пленарен доклад в международен форум, публикация в реферирано издание, индексирана в национален референтен списък