|Autors: Simeonova T., Tongov, M. T., Avdeev G.|
Title: Microstructure and properties of NiCrBSiC overlay coatings deposited by plasma scanning process
Keywords: NiCrBSiC coating, PTA scanning process, microstructure, hardness, overlaying.
Abstract: NiCrBSiC coatings on S275JR non-alloy structural steel substrate were produced using the plasma transferred arc (PTA) scanning process. Coatings were carried out by a preplaced powder method using a mixture of NiCrBSiC powder and a binder, painted over the substrate. The thickness of the coatings ranged from 1 to 2.5 mm due to the use of three different current densities (50, 65 and 80 A). Layers were produced under Ar atmosphere and cooled in air. Microstructural characterization studies were carried out by optical and scanning electron microscopy (SEM), X-ray diffraction (XRD) and microhardness measurements. They revealed the presence of a γ-Ni solid solution dendritic phase and interdendritic precipitates, which were found to be Ni3B and Cr23C6 particles. It is determined that the thickness of the coating layer increases with the current density and the concentration of the alloying elements decreases. Coatings are homogenous and no cracks or pores were detected in the interface..
1. Julieta Kaleicheva, Zdravka Karaguiozova, Valentin Mishev, Tribological Properties and Microstructure of Electroless Nickel Coatings Reinforced with Nanoparticles, Environment. Technology. Resources. Rezekne, Latvia Proceedings of the 12th International Scientific and Practical Conference. Volume III, pp. 88-91 - 2019 - в издания, индексирани в Scopus или Web of Science
2. V. DYAKOVA , P. TASHEV, M. KANDEVA, STUDY ON THE EFFECT OF NANOSIZED PARTICLES OF TiN AND SiC ON THE WEAR RESISTANCE, MICROSTRUCTURE AND CORROSION BEHAVIOR OF OVERLAY WELDMETAL, Journal of the Balkan Tribological Association VDPT 08.04.2019, ISSN 13104772 - 2019 - в издания, индексирани в Scopus или Web of Science
Вид: публикация в международен форум, публикация в издание с импакт фактор, публикация в реферирано издание, индексирана в Scopus