Abstract: Bimetallic Ni-Cu supported catalysts with different nickel (5–10 wt%) and copper (2.5–5 wt%) content were prepared by post-synthesis incipient wetness impregnation. 3D printing technique was applied for the catalysts preparation after modification with metal precursors. The catalysts were characterized by X-ray powder diffraction (XRD), Temperature programmed reduction with derivative thermogravimetry (TPR-DTG), N2 physisorption and Transmission electron microscopy (TEM). It was found that crystalline NixCuy intermetallic nanoparticles with different x/y ratio were formed in the reduced catalysts and they affected the reducibility and catalytic performance of the active nickel phases. The 3D printed catalysts were studied in the lignocellulosic biomass-derived levulinic acid (LA) to γ-valerolactone (GVL). It was found that the presence of NiCu alloy rich of nickel on the 3D printed catalysts favors their catalytic performance in the studied reaction. The preservation of the zeolite structure was detected for all 3D printed samples, which has a positive influence on the metal dispersion registered in the 3D spent catalysts. The 3D printed 10Ni5Cu/NaCaX catalyst showed the highest LA conversion and high GVL yield at 200 °C reaction temperature but more stable catalytic performance was registered for the 10Ni5Cu/NaX catalyst in 4 reaction cycles. The preservation of zeolite structure and metal dispersion in 3D printed 10Ni5Cu/NaX catalyst resulted in stable catalytic activity in the studied reaction indicating its potential for practical application.

References

1. Pambudi, N.A., Firdaus, R.A., Rizkiana, R., Ulfa, D.K., Salsabila, M.S., Suharno, Sukatiman, Renewable energy in Indonesia: current status, potential, and future development. Sustainability, 15, 2023, 2342, 10.3390/su15032342.
2. Popova, M., Dimitrov, M., Boycheva, S., Dimitrov, I., Ublekov, F., Koseva, N., Atanasova, G., Karashanova, D., Szegedi, Á., Ni-Cu and Ni-Co-modified fly ash zeolite catalysts for hydrodeoxygenation of levulinic acid to γ-valerolactone. Molecules, 29, 2024, 99, 10.3390/molecules29010099.
3. Obiora, N.K., Ujah, C.O., Asadu, C.O., Kolawole, F.O., Ekwueme, B.N., Production of hydrogen energy from biomass: prospects and challenges. GRETS, 2, 2024, 100100, 10.1016/j.grets.2024.100100.
4. Saberi Mehr, A., Ilkhani, M., Sabernia, S., Nooshmand, Sh, Ebrahimpour, A., Heydari, B., Thermodynamic modelling and optimisation of a green hydrogen-blendedsyngas-fueled integrated PV-SOFC system. Appl. Therm. Eng., 236, 2024, 121506, 10.1016/j.applthermaleng.2023.121506.
5. Lee, K., Jing, Y., Wang, Y., Yan, N., A unified view on catalytic conversion of biomass and waste plastics. Nat. Rev. Chem. 6 (2022), 635–652, 10.1038/s41570-022-00411-8.
6. Deng, W., Feng, Y., Fu, J., Guo, H., Guo, Y., Han, B., Jiang, Z., Kong, L., Li, C., Liu, H., et al. Catalytic conversion of lignocellulosic biomass into chemicals and fuels. Green. Energy Environ. 8 (2023), 10–114, 10.1016/j.gee.2022.07.003.
7. Mehrabadi, B.A.T., Eskandari, S., Khan, U., White, R.D., Regalbuto, J.R., Chapter one—a review of preparation methods for supported metal, catalysts. Adv. Catal. 61 (2017), 1–35, 10.1016/bs.acat.2017.10.001.
8. Wang, Z., Zhao, K., Xiao, B., Gao, P., He, D., Cai, T., Yuan, J., Fabrication of monolithic catalysts: comparison of the traditional and the novel green methods. Catalysts, 9, 2019, 981, 10.3390/catal9120981.
9. Klose, F., Scholz, P., Kreisel, G., Ondruschka, B., Kneise, R., Knopf, U., Catalysts from waste materials. Appl. Catal. B Environ. 28 (2000), 209–221, 10.1016/S0926-3373(00)00179-X.
10. Zhu, J., Wu, P., Chao, Y., Yu, J., Zhu, W., Liu, Z., Xu, C., Recent advances in 3D printing for catalytic applications. Chem. Eng. J., 433, 2022, 134341, 10.1016/j.cej.2021.134341.
11. Bogdan, E., Michorczyk, P., 3D printing in heterogeneous catalysis—the state of the art. Materials, 13, 2020, 4534, 10.3390/ma13204534.
12. Anekwe, I.M.S., Akpasi, S.O., Enemuo, E.M., Ashiegbu, D., Mustapha, S.I., Isa, Y.M., Innovations in catalytic understanding: a journey through advanced characterization. Mater. Today Catal., 7, 2024, 100061, 10.1016/j.mtcata.2024.100061.
13. Alarifi, I.M., Revolutionising fabrication advances and applications of 3D printing with composite materials: a review. Virtual Phys. Prototyp., 19, 2024, e2390504, 10.1080/17452759.2024.2390504.
14. Iftekar, S.F., Aabid, A., Amir, A., Baig, M., Advancements and limitations in 3D printing materials and technologies: a critical review. Polymers, 15, 2023, 2519, 10.3390/polym15112519.
15. Popova, M., Mladenov, B., Dimitrov, I., Dimitrov, M., Mitova, V., Mitrev, Y., Kovacheva, D., Velinov, N., Karashanova, D., Boycheva, S., 3D printed Ni–Cu sodalite catalysts for sustainable γ-valerolactone production from levulinic acid—effect of the copper content and the method of preparation. Processes, 13, 2025, 72, 10.3390/pr13010072.
16. Querol, X., Moreno, N., Umaña, J.C., Alastuey, A., Hernández, E., López-Soler, A., Plana, F., Synthesis of zeolites from coal fly ash: an overview. Int. J. Coal Geol. 50 (2002), 413–423, 10.1016/S0166-5162(02)00124-6.
17. Hong, J.L.X., Maneerung, T., Koh, S.N., Kawi, S., Wang, C.-H., Conversion of coal fly ash into zeolite materials: synthesis and characterizations, process design, and its cost-benefit analysis. Ind. Eng. Chem. Res. 56 (2017), 11565–11574, 10.1021/acs.iecr.7b02885.
18. Zhang, X., Li, C., Zheng, S., Yonghao, D., Zhiming, S., A review of the synthesis and application of zeolites from coal-based solid wastes. Int. J. Min. Met. Mater. 29 (2022), 1–21, 10.1007/s12613-021-2256-8.
19. Längauer, D., Čablík, V., Hredzák, S., Zubrik, A., Matik, M., Danková, Z., Preparation of synthetic zeolites from coal fly ash by hydrothermal synthesis. Mater, 14, 2021, 1267, 10.3390/ma14051267.
20. Koshlak, H., Synthesis of zeolites from coal fly ash using alkaline fusion and its applications in removing heavy metals. Mater, 16, 2023, 4837, 10.3390/ma16134837.
21. Zgureva, D., Stoyanova, V., Shoumkova, A., Boycheva, S., Avdeev, G., Quasi natural approach for crystallization of zeolites from different fly ashes and their application as adsorbent media for malachite green removal from polluted waters. Crystals, 10, 2020, 1064, 10.3390/cryst10111064.
22. Yao, Z.T., Ji, X.S., Sarker, P.K., Tang, J.H., Ge, L.Q., Xia, M.S., Xi, Y.Q., A comprehensive review on the applications of coal fly ash. EarthSci. Rev. 141 (2015), 105–121, 10.1016/j.earscirev.2014.11.016.
23. Jayaranjan, M.L.D., van Hullebusch, E., Annachhatre, A., Reuse options for coal fired power plant bottom ash and fly ash. Rev. Environ. Sci. Biotechnol. 13 (2014), 467–486, 10.1007/s11157-014-9336-4.
24. Yu, Y., Preparation of nanocrystalline TiO2-coated coal fly ash and effect of iron oxides in coal fly ash on photocatalytic activity. Powder Technol. 146 (2004), 154–159, 10.1016/j.powtec.2004.06.006.
25. ASTM C618-22 Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete, 2023, https://doi.org/10.1520/C0618-22.
26. Boycheva, S., Szegedi, Á., Lázár, K., Popov, C., Popova, M., Advanced high-iron coal fly ash zeolites for low-carbon emission catalytic combustion of VOCs. Catal. Today, 418, 2023, 114109, 10.1016/j.cattod.2023.114109.
27. Boycheva, S., Zgureva, D., Lazarova, H., Popova, M., Comparative studies of carbon capture onto coal fly ash zeolites Na-X and Na–Ca-X. Chemosphere, 271, 2021, 129505, 10.1016/j.chemosphere.2020.129505.
28. Belviso, C., Cavalcante, F., Lettino, A., Fiore, S., Effects of ultrasonic treatment on zeolite synthesized from coal fly ash. Ultrason. Sonochem. 18 (2011), 661–668, 10.1016/j.ultsonch.2010.08.011.
29. Boycheva, S., Marinov, I., Miteva, S., Zgureva, D., Conversion of coal fly ash into nanozeolite Na-X by applying ultrasound-assisted hydrothermal and fusion-hydrothermal alkaline activation. Sustain Chem. Pharm., 15, 2020, 100217, 10.1016/j.scp.2020.100217.
30. Thommes, M., Kaneko, K., Neimark, A.V., Olivier, J.P., Rodriguez-Reinoso, F., Rouquerol, J., Sing, K.S.W., Physisorption of gases, with special reference to the evaluation of surface area and pore size distribution (IUPAC Technical Report). Pure Appl. Chem. 87 (2015), 1051–1069, 10.1515/pac-2014-1117.
31. Pinheiro, A.N., Valentini, A., Sasaki, J.M., Oliveira, A.C., Highly stable dealuminated zeolite support for the production of hydrogen by dry reforming of methane. Appl. Catal. A 355 (2009), 156–168, 10.1016/j.apcata.2008.12.007.
32. Boycheva, S., Chakarova, K., Mihaylov, M., Hadjiivanov, K., Popova, M., Effect of calcium on enhanced carbon capture potential of coal fly ash zeolites. Part II: a study on the adsorption mechanisms. Environ. Sci. Process. Impacts, 24, 2022, 1934, 10.1039/D2EM00252C.

Issue

Copyright Elsevier B.V.